Wear resistance of smooth TiO2 coating obtained by anodic oxidation and sol-gel dip-coating combination - Research Data & Supplemental Files
; Rosenberger, Mario Roberto ; Schvezov, Carlos Enrique ; Vera, Maria Laura Otros responsables
Fecha
Publicador:
Consejo Nacional de Investigaciones Científicas y Técnicas
Fecha de depósito:
4/05/2023
Fecha de creación:
1/1/2016-1/3/2023
Clasificación temática
Palabras clave
Resumen
The data represents the results of wear tests using a reciprocating ball-on-flat equipment. The counterpart was a conical, hemispherical tip with a radius of 10 microns. The counterpart oscillated at 0.7 Hz with an amplitude of 4 mm. The loads applied were 39, 78, 117, and 156 mN for 1, 2, 3, and 4 minutes, respectively. The tests were conducted at 22 ± 2 °C, with 40 ± 10% humidity, and without lubrication.
Colecciones
Condiciones de uso
Las buenas prácticas científicas esperan que se otorgue el crédito adecuado mediante una citación. Utilice un formato de citación y aplique estas normas de reutilización:
Licencia Creative Commons
Excepto donde se indique lo contrario, la licencia de este ítem se describe como by-nc-sa
Archivos
ARCHIVO
NOTAS DE USO
TAMAÑO
Complete_scars_of_TI__TASS_and_TSS__Tests_L78-t4__L117-t3_and_L117-t4.pdf
figura de las escaras de desgaste
634.84 KB
experimental_data_-_scar_width__2r____counterpart_penetration__d_.xlsx
datos de las escaras de desgaste
33.55 KB
Images_of_a_representative_part_of_the_wear_scars_for_all_tests_performed.pdf
detalle de las escaras.
1.15 MB
Schematic_diagram_of_the_process_of_obtaining_the_wear_volume.pdf
esquema del procedimiento de cálculo
112.21 KB