Fabricación de vidrios metálicos base cobre: evolución de las fases durante el Proceso de aleación mecánica

Título: Production of Copper-based Metallic Glasses: Evolution of the Phases During Mechanical Alloying
Rojas, Paula; Martínez, Carola; Viancos, Francisco; Aguilar, Claudio; Guzmán, Danny ; Zelaya, Maria EugeniaIcon
Fecha de publicación: 06/2015
Editorial: Univ Fed Rio de Janeiro
Revista: Revista Matéria
e-ISSN: 1517-7076
Idioma: Español
Tipo de recurso: Artículo publicado
Clasificación temática:
Ingeniería de los Materiales; Ingeniería de los Materiales

Resumen

 
En este estudio se fabricaron diferentes materiales (base cobre) bajo las mismas condiciones de molienda: molino empleado fue un SPEX 8000D, atmósfera de argón, acido esteárico, RBP=10:1, con tiempos varia-bles desde 1 hasta 120 horas, con el objetivo de comparar los cambios microestructurales durante el proceso de: Cobre puro, Aleaciones Cu-Ni, Aleaciones Cu-Zr y aleaciones Cu-Ni-Zr. Las muestras, tras la molienda, fueron analizadas mediante difracción de rayos X, microscopía electrónica de transmisión y calorimetría dife-rencial de barrido. De acuerdo a los resultados, el cobre al ser sometido al proceso alcanza un tamaño de cris-talita que se hace asintótico a partir de las 5 horas, mientras que en el sistema Cu-Ni, en vez de apreciarse un refinamiento microestructural a ese mismo periodo, se advierte una total solubilización del níquel en cobre (40-60 y 50-50) y de cobre en níquel (60-40). Por su parte, en el sistema binario Cu-Zr, se encontró, tam-bién para 5 horas, que el sistema estaba prácticamente amorfizado (60-40 y 50-50) al igual que en el caso de las aleaciones ternarias Cu-Ni-Zr (60-10-30 y 50-10-40).
 
In this study, different, copper-based materials were fabricated under equal milling conditions (SPEX 8000D, argon atmosphere, stearic acid, BPR=10:1) and variable amounts of time, from 1 to 120 hours, in order to compare the microstructural changes during the process. The materials were: Pure copper; Cu-Ni alloys; CuZr alloys; and Cu-Ni-Zr alloys. Subsequent to milling, the samples were measured with X-Ray Diffraction, Electron Transmission Microscopy, and Differential Scanning Calorimetry. According to the results, copper, upon being subjected to the process, reaches a crystallite size that tends towards an asymptote starting at 5 hours. In the Cu-Ni system, instead of observing a microstructural refinement during this same period, there was rather a total solubilization of the nickel into the copper (40-60 and50-50), and of the copper into the nickel (60-40). As for the Cu-Zr binary system, it was found that, for five hours as well, the system was practically amorphous (60-40 and 50-50), a condition also present in the Cu-Ni-Zr ternary alloys (60-10-30 and 50-10-40).
 
Palabras clave: Aleaciones Base Cobre , Vidrios Metálicos , Aleado Metálico
Ver el registro completo
 
Archivos asociados
Thumbnail
 
Tamaño: 985.0Kb
Formato: PDF
.
Descargar
Licencia
info:eu-repo/semantics/openAccess Excepto donde se diga explícitamente, este item se publica bajo la siguiente descripción: Creative Commons Attribution-NonCommercial-ShareAlike 2.5 Unported (CC BY-NC-SA 2.5)
Identificadores
URI: http://hdl.handle.net/11336/9146
URL: http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1517-70762015000300705&l
DOI: http://dx.doi.org/10.1590/S1517-707620150003.0074
Colecciones
Articulos(CCT - PATAGONIA NORTE)
Articulos de CTRO.CIENTIFICO TECNOL.CONICET - PATAGONIA NORTE
Citación
Rojas, Paula; Martínez, Carola; Viancos, Francisco; Aguilar, Claudio; Guzmán, Danny ; et al.; Fabricación de vidrios metálicos base cobre: evolución de las fases durante el Proceso de aleación mecánica; Univ Fed Rio de Janeiro; Revista Matéria; 20; 3; 6-2015; 705-713
Compartir
Altmétricas
 

Enviar por e-mail
Separar cada destinatario (hasta 5) con punto y coma.
  • Facebook
  • X Conicet Digital
  • Instagram
  • YouTube
  • Sound Cloud
  • LinkedIn

Los contenidos del CONICET están licenciados bajo Creative Commons Reconocimiento 2.5 Argentina License

https://www.conicet.gov.ar/ - CONICET

Inicio

Explorar

  • Autores
  • Disciplinas
  • Comunidades

Estadísticas

Novedades

  • Noticias
  • Boletines

Ayuda

Acerca de

  • CONICET Digital
  • Equipo
  • Red Federal

Contacto

Godoy Cruz 2290 (C1425FQB) CABA – República Argentina – Tel: +5411 4899-5400 repositorio@conicet.gov.ar
TÉRMINOS Y CONDICIONES