Portland blended cements: Demolition ceramic waste management

Abstract

Demolition ceramic wastes (DCWs) were investigated in order to determine their potential use as supplementary cementitious materials in Portland Blended Cements (PBCs). For this purpose, three ceramic wastes were investigated. After characterization of the materials used, the effect of ceramic waste replacement (8, 24 and 40% by mass) was analyzed. Pozzolanic activity, hydration progress, workability and compressive strength were determined at 2, 7 and 28 days. The results showed that the ground wastes behave as filler at an early age, but as hydration progresses, the pozzolanic activity of ceramic waste contributes to the strength requirement.

Se estudiaron residuos cerámicos de demolición (DCWs) a fin de determinar su potencial uso como materiales cementicios suplementarios en cementos mezcla (PBC). Para este propósito, se investigaron tres residuos cerámicos. Luego de la caracterización de los materiales a utilizar, se analizó el efecto del reemplazo por residuos cerámico (8, 24 y 40% en peso). Se estudió la actividad puzolánica, el progreso de la hidratación, la trabajabilidad y la resistencia a compresión a 2, 7 y 28 días. Los resultados mostraron que los residuos molidos se comportaron como fillers a edades tempranas, pero con el progreso de la hidratación, la actividad puzolánica de los residuos cerámicos contribuye a los requerimientos de resistencia.