Barrier Properties and Structural Study of Nanocomposite of HDPE/Montmorillonite Modified with Polyvinylalcohol

Abstract

In this work was studied the permeation of CO2 in films of high-density polyethylene (HDPE) and organoclay modified with polyvinylalcohol (MMTHDTMA/PVA) obtained frommelt blending. Permeation study showed that the incorporation of the modified organoclay generates a significant effect on the barrier properties of HDPE. When a load of 2wt% of MMTHDTMA/PVA was incorporated in the polymer matrix, the flow of CO2 decreased 43.7% compared to pure polyethylene.The results of TEM showed that clay layers were dispersed in the polymeric matrix, obtaining an exfoliated-structure nanocomposite. The thermal stability of nanocomposite was significantly enhanced with respect to the pristine HDPE. DSC results showed that the crystallinity was maintained as the pure polymericmatrix. Consequently, the decrease of permeability was attributable only to the effect of tortuosity generated by the dispersion ofMMTHDTMA/PVA. Notably the mechanical properties remain equal to those of pure polyethylene, but with an increase in barrier properties to CO2. This procedure allows obtaining nanocomposites of HDPE with a good barrierproperty to CO2 which would make it competitive in the use of packaging. with an increase in barrier properties to CO2. This procedure allows obtaining nanocomposites of HDPE with a good barrier property to CO2 which would make it competitive in the use of packaging.