Artículo
Steam-methane reforming at low temperature on nickel-based catalysts
Nieva, Maria Alejandra
; Villaverde, María Magdalena
; Monzón Bescós, Antonio; Garetto, Teresita Francisca
; Marchi, Alberto Julio
![Icon](/themes/CONICETDigital/images/conicet.png)
![Icon](/themes/CONICETDigital/images/conicet.png)
![Icon](/themes/CONICETDigital/images/conicet.png)
![Icon](/themes/CONICETDigital/images/conicet.png)
Fecha de publicación:
09/2013
Editorial:
Elsevier
Revista:
Chemical Engineering Journal
ISSN:
1385-8947
Idioma:
Inglés
Tipo de recurso:
Artículo publicado
Clasificación temática:
Resumen
In this work, we report the activity results obtained in steam-methane reforming (SMR) at 500 and 600 °C using four nickel-based catalysts: (a) Ni/Al2O3 and Ni/SiO2, prepared by incipient wetness impregnation method and (b) Ni-Zn-Al and Ni-Mg-Al, prepared by coprecipitation method. In all of the samples, the nickel load ranged between 7% and 9%. The catalytic activity in SMR at steady state followed the pattern: Ni-Mg-Al = Ni-Zn-Al > Ni/Al2O3 > Ni/SiO2. According to characterization results, the interaction between Ni2+ species and support in precursor oxides was stronger in Ni-Mg-Al and Ni-Zn-Al than in Ni/Al2O3 and Ni/SiO2. After activation in H2 flow, large metal nickel particles with low or none interaction with the support were obtained in the case of Ni/Al2O3 and Ni/SiO2. On the contrary, small metal particles, between 3 and 6 nm, in high interaction with support were obtained in Ni-Zn-Al and Ni-Mg-Al catalysts. The metal phase formed in Ni-Mg-Al and Ni-Zn-Al was the most active and resistant to sintering under reaction conditions at T < 600 °C. It was also found that carbon nanofibers were formed on Ni/Al2O3, Ni/SiO2 and Ni-Mg-Al catalysts during SMR at 600 °C. The amount and diameter of nanofibers formed on Ni-Mg-Al were lower than on catalysts prepared by impregnation method, which is in agreement with the relative sizes of metal nickel particles in each case. Amazingly, no filamentary carbon was detected on the used Ni-Zn-Al sample: only amorphous coke in low amounts was formed. This was attributed to the proper interaction of small metal nickel particles with the non-stoichiometric zinc aluminate-like phase formed after thermal treatments of catalyst precursor.
Archivos asociados
Licencia
Identificadores
Colecciones
Articulos(INCAPE)
Articulos de INST.DE INVEST.EN CATALISIS Y PETROQUIMICA "ING. JOSE MIGUEL PARERA"
Articulos de INST.DE INVEST.EN CATALISIS Y PETROQUIMICA "ING. JOSE MIGUEL PARERA"
Citación
Marchi, Alberto Julio; Garetto, Teresita Francisca; Monzón Bescós, Antonio; Villaverde, María Magdalena; Nieva, Maria Alejandra; Steam-methane reforming at low temperature on nickel-based catalysts; Elsevier; Chemical Engineering Journal; 235; 9-2013; 158-166
Compartir
Altmétricas