Dissimilar Friction Stir Lap Welding of Aluminium to Steel: Influence of Alloy Type and Sheet Thickness on Strain Distribution and Failure Location

Abstract

Dissimilar joining through solid-state welding is an important engineering tool to addressthe transportation industry’s sustainable goals. The dissimilar friction stir lap welding (FSLW) of two different aluminium alloys (AA5182 and AA5052 with two different thicknesses) to steels AISI1010 and DP1000 was performed in this work, in order to analyse the effect of the mismatch in base material properties and plate thickness on the joint strength and fracture location. The mechanical behaviour and the strength of the welds were assessed using transverse tensile–shear testing and hardness measurements. Strain data acquisition through Digital Image Correlation (DIC) was used. The differences in fracture location registered for the different joints are explained based on the alloy’s plastic properties and on the mismatch in thickness between the plates. Local stress–strain curves were plotted, using the strain data acquired through DIC, to highlight the mechanisms resulting in the differences in tensile behaviour among the joints. It is concluded that despite the differences in failure location and tensile behaviour, the strength of the joints was very similar, irrespective of the base material combinations.