FMR evidence of strong uniaxial anisotropy in La1-xCaxMnO3

Abstract

We report an electron spin resonance study on La1-xCaxMnO3 ceramic samples with x = 0.33 and 0.5. Below TC the absorption line-shape can be well described as a ferromagnetic resonance with randomly distributed uniaxial anisotropy. In both samples the line-shape is used to fit an average anisotropy value. The anisotropy changes from easy plane for x = 0.33 to easy axis for x = 0.5. The present results for x = 0.5 imply that the uniaxial anisotropy, obtained from the measurements at 100K, is larger than the one expected for shape-only contribution even considering the extreme case of nanowires. The origin and magnitude of this anisotropy are discussed.

Presentamos un estudio mediante resonancia electronica de esp ´ ´ın en muestras ceramicas de La ´ 1−xCaxMnO3 con x = 0.33 y 0.5. Por debajo de Tc la l´ınea de absorcion puede describirse como una resonancia ferromagn ´ etica con eje de anisotrop ´ ´ıa uniaxial distribuido al azar. En ambas muestras la forma de l´ınea se usa para ajustar una anisotrop´ıa promedio. La anisotrop´ıa cambia de plano facil, para x = 0.33 a eje f ´ acil ´ para x = 0.5. Los resultados para x = 0.5 implican que la anisotrop´ıa uniaxial, obtenida de mediciones a 100K, es mayor que la esperable para contribuciones debidas solo a la forma, a ´ un considerando el caso extremo de nanohilos. El origen y la magnitud de esta anisotrop ´ ´ıa son discutidas.