Relaxor behavior of the conductive process for the system Pb0,91La0,09(Zr0,65Ti0,35)O3 + xMnO

Abstract

In this work, a study of the ceramic Pb0,91La0,09(Zr0,65Ti0,35)O3 + xMnO with x = 0,0; 0,01; 0,02 and 0,03 was carried out, The dielectric response of PLZT was measured using the impedance spectroscopy method, in the frequency range from 100 Hz to 10 MHz and at temperatures from 15 to 700 K, In the behavior of permittivity with frequency, a strong dispersion is reported for x = 0,0, This relaxing behavior becomes imperceptible with the increase of the Mn2+ cation, In the temperature range between 660 and 700 K, the doped samples showed a relaxation process by conductivity, studied by the Cole-Cole relaxation function, determining, in addition, the thermal evolution of the relaxation time τ, suggesting conductive processes by ion movement. The macroscopic activation energy was determined indicating a conduction process by oxygen vacancies.

En este trabajo se realiza un estudio de la cerámica Pb0,91La0,09(Zr0,65Ti0,35)O3 + xMnO con x = 0,0; 0,01; 0,02 y 0,03. La respuesta dieléctrica del PLZT es medida a través del método de espectroscopia de impedancia, en un rango de frecuencias 100 Hz a 10 MHz y a temperaturas desde 15 a 700 K. En el comportamiento de la permitividad con la frecuencia se reporta una fuerte dispersión para x = 0,0. Este comportamiento relajador se hace imperceptible con el aumento del catión Mn2+.En el intervalo de temperaturas comprendido entre los 660 y 700 K las muestras dopadas, manifestaron un proceso de relajación por conductividad, estudiado por la función de relajación Cole-Cole, determinándose, además, la evolución térmica del tiempo de relajación sugiriendo procesos conductivos por movimiento de iones. Se determinó la energía de activación macroscópica indicando un proceso de conducción por vacancias de oxígeno.