Ex Vivo Microleakage Comparison between Glass Ionomers used as Pit and Fissure Sealant

Abstract

The aim of this study was to evaluate in vitro the marginal microleakage of two glass ionomer materials used as pit and fissure sealants. Thirty healthy premolars extracted for orthodontic treatment were randomly assigned to two groups (n=15) and respectively sealed with two glass ionomers (Group I, Fuji VII and Group II, Fuji IX). All teeth were preserved in artificial saliva (NAF) for 10 days, thermocycled (250 cycles; 5oC, 37oC and 60oC), isolated, and immersed in 2% alcohol gentian violet blue solution for 24 h. After washing, teeth were included in acrylic resin and sectioned longitudinally in a bucco-lingual direction with a Struers-Minitom cutting device. Samples were analyzed for leakage using an optical microscope (Olympus BX- 60M). TheWilliams and Winter semi-quantitative ranked scale was used to score dye penetration. In Group I the grades were distributedasfollows:Grade1,1sampleandGrade3,14samples (Mean 2.87 Median 3, SD 0.52). In Group II: Grade 0: 4 samples, Grade 1, 3 samples, Grade 2, 2 samples and Grade 3, 6 samples (Mean 1.67, Median 2, SD 1.29). Fisher’s exact test showed statistically significant differences between materials (p=0.006). From these results, we conclude that Fuji IX had better marginal sealing than Fuji VII when used as a pit and fissure sealant.

El objetivo del trabajo fue comparar la eficacia como sellador de dos ionomeros vitreos. Se emplearon 30 premolares sanos extraidos por razones ortodoncicas. Se dividieron en dos grupos iguales (n=15) .Grupo I: Fuji VII y Grupo II: Fuji IX. Los dientes, fueron conservados en saliva artificial (NAF) durante 10 dias. Luego, fueron termociclados (250 ciclos) a 5oC, 37oC y 60oC. Posteriormente se sumergieron en violeta de genciana durante 24 hs. Una vez lavadas las muestras se seccionaron y evaluaron con el criterio de Williams y Winter, utilizando un microscopio optico (Olympus BX-60M) para valorar la penetracion del colorante. Los grados obtenidos para cada grupo fueron: en Grupo I (Fuji VII), Grado 1, 1 muestra y Grado 3, 14 muestras (Media 2,87, Mediana 3 y SD 0.52). En el Grupo II (Fuji IX) los grados se distribuyeron asi: Grado 0, 4 muestras, Grado 1, 3 muestras, Grado 2, 2 muestras y Grado 3, 6 muestras. (Media 1.67, Mediana 2 y SD 1.29). La Prueba exacta de Fisher (p=0,006) demostro diferencias estadisticamente significativa entre materiales. Se concluyo que el mejor sellado marginal fue obtenido utilizando el material Fuji IX comparado con Fuji VII cuando es utilizado como sellador.