Occupancy of 4d-states in T (T: Mo, Nb) from NEXAFS L3,2 Spectra of Nd-Fe-B-T Alloys

Abstract

Samples of NdyFe(86–-y–x)B14Tx (T: Mo, Nb; x = 2, 4; y = 7, 8) alloys were studied by X-ray absorption spectroscopy. The NEXAFS spectra of NdFeB ribbons produced by the melt spinning technique (as quenched, AQ) and subsequently annealed (TT) were taken at Mo and Nb L3,2-edge. We calculated the variations in occupancy of the 4d-states (in both additives), finding an opposite trend in their filling. The most significant changes were observed in the T2Nd7 system, for which the electron occupancy in the 4d levels was modified to an excess of 1 electron/atom (after thermal treatment). The correlation between these results and magnetic features of the alloys are evidenced.

Сплавы NdyFe(86-y-x)B14Tx (T: Mo, Nb; x = 2, 4; y =7, 8) изучены методом рентгеновской абсорбционной спектроскопии. Образцы имели форму полосок, полученных методом вытягивания из расплава (в состоя- нии после закалки), а затем отожженных. Тонкая структура рентгеновских спектров поглощения спла- вов NdFeB исследована вблизи границы L3,2 Мо и Nb. Рассчитаны изменения заселенности 4d-состояний (в обеих примесях) и обнаружены противоположные тенденции в их заполнении. Наиболее существенные изменения наблюдались в системе T2Nd7, где заселенность 4d-уровня изменялась более чем на 1 элект- рон/атом (после термообработки). Корреляция между этими результатами и магнитными характерис- тиками исследованных сплавов очевидна