Properties of polyethersulfone ultrafiltration membranes modified with polyethylene glycols
Méndez, Mercedes Liliana
; Romero, Analía Irma
; Rajal, Verónica Beatriz
; Castro Vidaurre, Elza Fani; Calvo, José I.; Palacio, Laura; Hernandez, Antonio
![Icon](/themes/CONICETDigital/images/conicet.png)
![Icon](/themes/CONICETDigital/images/conicet.png)
![Icon](/themes/CONICETDigital/images/conicet.png)
Fecha de publicación:
04/2013
Editorial:
John Wiley & Sons Inc
Revista:
Polymer Engineering and Science
ISSN:
0032-3888
Idioma:
Inglés
Tipo de recurso:
Artículo publicado
Clasificación temática:
Resumen
Polyethersulfone ultrafiltration membranes have been prepared using polyethylene glycols (PEGs) of 400, 1000, and 10,000 gmol, as additive with dimethylacetamide as solvent. Infrared analysis proves that PEG leaves almost completely the surface of the membranes after 24 h of water immersion. Scanning electron microscopy, contact angle, and liquid-liquid displacement porometry have been used to characterize the membrane morphology, surface hydrophilicity and porous structure. The relative flux reduction factor, flux, retention - of PEG (20,000 and 35,000 g/mol) and bovine serum albumin (67,000 g/mol) - and pure water permeability have been measured for the membranes. Results show that the addition of PEG increases slightly hydrophilicity and decreases pore size and narrows the corresponding pore size distribution while thickening the skin layer, in spite of the fast disappearance of the added PEG form the membrane surface. The resulting flux and pure water permeability are higher when middle size PEGs are added but decrease again when very high molecular weight (MW) PEGs are added. Retention decreases initially for increasing MWs of PEG although for very long PEG chains (MW of 10,000 g/mol) retention increases again. After filtration, the membranes with PEG added showed a lower relative flux reduction that decreases for increasing MW of the added PEGs.
Archivos asociados
Licencia
Identificadores
Colecciones
Articulos(INIQUI)
Articulos de INST.DE INVEST.PARA LA INDUSTRIA QUIMICA (I)
Articulos de INST.DE INVEST.PARA LA INDUSTRIA QUIMICA (I)
Citación
Méndez, Mercedes Liliana; Romero, Analía Irma; Rajal, Verónica Beatriz; Castro Vidaurre, Elza Fani; Calvo, José I.; et al.; Properties of polyethersulfone ultrafiltration membranes modified with polyethylene glycols; John Wiley & Sons Inc; Polymer Engineering and Science; 54; 5; 4-2013; 1211-1221
Compartir
Altmétricas