Curing behavior and properties of high biosourced epoxy resin blends based on a triepoxy monomer and a tricarboxylic acid hardener from 10-undecenoic acid

Abstract

Renewable propane-1,2,3-triyl tris(9-(oxiran-2-yl) nonanoate) (EGU, 100 wt% biogenic) and a tricarboxylic acid triglyceride (CGTU) hardener (85.7 wt% biogenic) were synthesized from 10-undecenoic acid (10-UDA) and used to produce epoxy resins with 52–92 wt% biobased carbon. CGTU was prepared by thermally activated thiol-ene coupling of thioglycolic acid onto propane-1,2,3-triyl tris(undec-10-enoate), (GUD) in the absence of solvent. The characterized CGTU was used as a green hardener of blends based on EGU and a conventional bisphenol A-based epoxy pre-polymer (DGEBA) at various mass percentages (0–100 wt%) with an stoichiometric epoxy/acid equivalent ratio. Calorimetric studies revealed higher peak temperature, lower reaction heats, and longer gelation times in resins with high EGU proportion, evidencing the lower reactivity of aliphatic EGU compared with aromatic DGEBA. Cured resins were yellowish transparent rubber-like materials with glass transition temperatures (Tg) varying from −14 °C to −42 °C and tensile strength in the range of 1750 kPa–790 kPa, for 0 and 100 wt % EGU, respectively. The soluble fraction of all resins was less than 4.3%, reflecting a high level of crosslinking. Thermosets with high biobased content showed both UV-light protection and visible light transparency.